low pressure metal-organic vapor-phase (MOVPE) and plasma-assisted molecular beam epitaxial (PA-MBE) grown structures with an Al-content between 12% and 30% yield carrier concentrations from 3.6×1012 to 1.2×1013 cm−2. A difference of the concentrations for a fixed Al-content was found between the different epitaxial techniques. This result indicates unambiguously different surface potentials determined quantitatively from the carrier concentration, and is verified in addition by the results of photoreflectance spectroscopy. The GaN surface potentials of MOVPE and PA-MBE grown samples amounts to (0.26±0.04) and (0.61±0.10) eV irrespective of the Al-content of the barrier layer. After device fabrication, we find that due to the identical surface potential defined by the Ni Schottky gate, the threshold voltage for a given Al-content is the same for samples grown with different techniques. Thus, the interplay between epitaxy and process technology defines the threshold voltage.